Effects of ${AI_2O_3}/{P_2O_5}$ ratio on the crystallization of a series of glasses with the nominal composition of 41.4wt % $SiO_2$, 35.0wt % CaO, 20.6wt % (${P_2O_5}$+${AI_2O_3}$) and 3.0wt% MgO were investigated with DTA, XRD and SEM. The major crystalline phases are apatite and anorthite. The glass transition temperature ($T_g$) and the softening point ($T_s$) are shifted to the upper temperature by increasing $AI_2O_3$ content. The temperature of apatite crystallization ($T_{p1}$) is increased by $AI_2O_3$ content, but the tempera¬ture of anorthite crystallization ($T_{p2}$) is not affected significantly. With increased of $AI_2O_3$, the apatite crystallization is decreased, but anorthite crystallization is increased.