The humidity-sensitive specimens-(BaS11T-S1xTCaS1xT)TiOS13T, x=0, 0.1, 0.2, 0.3, 0.4, 0.5-were fabricated by a solid-state reaction method which is easy in process control of microstructure and good in mass production, and their humidity-sensitive characteristics were examined. Ca inhibits grain growth and the open porosity increases with Ca substitution, and the specimens at x=0.5 show the best humidity sensitivity. Their humidity sensitivity is higher at the lower frequencies, and drift phenomenon in humidity sensitivity is exhibted with aging in the air, which disappears by a heat treatment. The electrical conduction with water adsorption is dominated by the ions, and the activation energy decreases with increasing relative humidity.