The dislocation configuration in web-grown silicon ribbon was investigated using chemical etching techniques. The presence of dislocation loops on twin planes is observed and acounted for by self-interstitial condensation. The interstitials were either quenched in, due to the rapid cooling of the ribbon from the solidification temperatures, or produced by oxide precipitation on the twin plane. Very large faulted loops of mm size were also observed.