W-Ti-C-N based multiphase hard materials have been prepared from WC/TiN powder mixture. By sintering at and above 190$0^{circ}C$, the two phases of powder mixture has transformed into intermixed W, W2C and Ti(C, N) phases. For the temperature range between 180$0^{circ}C$ and 210$0^{circ}C$, the sintered or hot pressed samples show maximum density and hardness. The seems that metallic W grains enhance the fracture toughness of materials. The wear resistance of the material is found to increase with increasing hardness.