Mn-Zn ferrite powder was obtained by wet method that was to be coprecipitated the metal ions of Fe2+, Mn2+ and Zn2+ with alkali solution. The target composition of the ferrite powder was 52 mol% Fe2O3, 24 mol% MnO, and 24 mol% ZnO, that was based on the region of high permeability. And the other ferrite powder was prepared by the dry method that was to be mixed the metal oxides as the above chemical composition. The wet method was compared with dry method for the powder properties and the electromagnetic characteristics of sintered cores. The synthesized powder by wet method was smaller particle size, narrower particle distribution, and higher purity than that of dry method. The initial permeability of sintered sample prepared by the wet method was 14000~28000, on the other side, 9000~15500 in case of the dry method.