Intermetallic Ti-Si system ceramics were synthesized from stochiometric mixtures of titanium and silicone powders in vacuum by Self-propagating High-temperature Synthesis(SHS). In each cases of Ti5Si3, Ti5Si4 and TiSi, and TiSi2 synthesis, 20wt% product dilution, direct ignition and SHS chemical furnace method were employed. The combustion modes, which were observed during the synthesis process by using the high speed camera, of Ti5Si3, Ti5Si4, TiSi, and TiSi2 exhibit spin, osciallatory, steady-state, and spin combustion, respectively. With increasing Ti/Si molar ratio an decrease of combustion velocities was found. From the results on the measurement of the flexural strength, the specimen hot pressed at 135$0^{circ}C$ for 30 min using synthesized Ti5Si4 powders showed the highest flexural strength at 215 MPa.