In a salb-preheating furnace of steel-making industry, the oxidation/degradation behavior of Cr3C2 ceramic composited dkid button reaction with scale in Fe-oxide system occurs and was thermodynamically examined. The reaction of scale with Cr3C2 skid button produces Cr3C2(s) and C(s), and Co gas is then evolved from the reaction of C(s) with Fe-scale. Cr3C2(s) from oxidation of Cr3C2(s) reacted with Fe-oxide(s) becomes high-melting chromite. The chromite acts as protection layer against further oxidation and improves resistance of the reaction of Cr3C2 skid button with Fe-scale.