CaO-Al2O3 glass is a good candidate as optical fiber amplifier and laser. In this study, optical properties for 4I13/2longrightarrow4I15/2 transition of Er3+ ions doped in CaO-Al2O3 glasses were investigated. Optical absorptions, radiative transition probabilities and lifetimes for 4I13/2 level were evaluated by using Judd-Ofelt theory. Also, induced- emmision cross-sections of 4I13/2longrightarrow4I15/2 transition were calculated. Radiative transition probability and lifetime of 4I13/2 level were 144.6s-1, 690$mutextrm{s}$ respectively for 60CaO.40Al2O3 glass(FS0) and 152.6s-1, 660 $mutextrm{s}$ for 54 CaO.36Al2O3.10SiO2 glass (FS10). Each induced-emission cross sections for FS0 and FS10 was 0.749$ imes$10-20 $ extrm{cm}^2$, 0.892$ imes$10-20 $ extrm{cm}^2$. Obtained values were comparable with those of ZBLA glass studied as optical fiber amplifier and laser material.