To increase the anti-oxidation and anti-wear properties of graphite for the propellant-burning environment, SiC, Pt and Al2O3 multi-layer coatings were conducted succesisvely and the optimum condition was researched. The SiC layer was produced by pack cementation and SiC layer in thickness of 30 ${mu}{ extrm}{m}$ coating was produced after coating for 6 hours. Pt layer was coated by sputtering, and the Al2O3 layer was coated by reactive sputtering. the thickness of Pt layer and Al2O3 layer was less than one-tenth of that of SiC layer. The pack coated specimens and multi-layer coated specimens were made using above conditions and test-fired. The test result showed that the wear rate of SiC layer is approximately 1/10 compared to that of uncoated graphite.