Crystallizable glasses with precipitation of celsian were prepared for the purpose of insulating dielectric layers for the devices such as integrated circuit substrates. Crystallization behavior of these glasses were studied by DTA, SEM, XRD analysis and by the measurement of dielectric properties. The base composition of the glass-ceramic consists in weight percent of 30% SiO2, 10% Al2O3, 26% BaO, 10% CaO, 10% ZnO, 8%TiO2 and 6% B2O3. 2-6 wt% Y2O3 were selected as the nucleating agent to promote monoclinic celsian formation. As a result, in barium-rich glasses containing 4~6wt% Y2O3 , monoclinic celsian was developed as major crystalline phase in the temperature range of 850~90$0^{circ}C$. Also, the dielectric constant and quality factor of these glass-ceramics were about 9 and more than 1000, respectively.