Pb(Mg1/3Nb2/3)O3-PbTiO3-BaTiO3 solid solution was formed by mixed-oxide method. The phase during formation was analysed by XRD and formation mechanism was investigated. While heat-treating Pb(Mg1/3Nb2/3)O3 composition, the first, Pb2Nb2O7 and Pb3Nb2O8 pyrochlore phases are formed, and finally Pb(Mg1/3Nb2/3)O3 perovskite phase with containing Pb3Nb4O13 pyrochlore phase is obtained at 80$0^{circ}C$. When Pb(Mg1/3Nb2/3)O3 composition is modified with PbTiO3 which have strong ionic bonding and high tolerance factor, the amount of pyrochlore phase is decreased by increasing of stability in perovskite structure.