Mechanical properties of hot-pressed SiC whisker/Al2O3 composites were strongly dependent on the granular characteristics of mixed powder, which were controlled by co-dispersion condition, the existence of steric barrier on whisker surface, and granulating method, etc. Heat-treatment of SiC whiskers at $700^{circ}C$ for 1 hr in air was very effective both for achieving dispersion stability of whiskers with PVA adsorption and for obtaining excellent mechanical properties of resulting composites. It is believed from the fractography of composites prepared with various whisker dispersion conditions that the most common fracture origin of Al2O3 agglomerate could be attributed to whisker clusters arising due to flocculation. Further improvement of mechanical properties of composites were achieved by hot pressing green tapes prepared by Doctor-blade process, which promoted two-dimensional random alignment of whiskers.