The purpose of this study is to investigate the Improvement of fiber surface, tenacity & elogation, fabric counts, thickness, handle, moisture regain, static voltage, handle, dyeability when polyester fabrics are treated with NaOH solution adding quartemary ammonium salt (Benzyl dimetyl dodecyl ammonium chloride . BDMDAC) The results are as follows. I. In regard to the method of processing VET, when the PET fabrics are alkaline-hydrolyzed adding BDMDAC, the weight loss of PET fabrics increased remarkably to the increse of BDMDAC concentration than when they are treated only in NaOH solution. When PET fabrics are alkaline-hydrolyzed the amount of BDMDAC as the catalyst is proper lg/1 II. The change in physical & chemical properties of alkaline-hydrolyzed PET fabrirs. 1. As the amount of the weight loss on PET fabrics increased, the void space of the PET yale increased but tenacity & elongation and thickness decreased. 2. The fabric counts of PET increased due to shrinkage by alkaline-hydrolydzing. 3. As the amount of of the weight loss on PET fabrics increased. NUMERI, FUKURAMI, increaseed and KOSHI decreased and Total hand value(T.H.V) in all cases increaseed. When the weight Ioss is 30.9% T.H.V. is best. 4. Moisture regain of PET fabrics a little increased by alkaline-hydrolyzing treatment. As the weight loss increased, static voltage is decreased. 5. The last dye absorption is different according to the degree of the Affinity. In regard to the difference of dye color, the dyestuff of low molecular weight dyed for deep color.