Films of glass-ceramics $Li_2O-Al_2O_3-SiO_2$(LAS)system were prepared on substrate of an iron plate(SCP) by sol-gel technique using metal alkoxide such as Si$(OC_2H_5)_4$,Al$(OC_2H_9)_3$) and Ti$(OC_2H_6)_4$). Sol which was made by means of simple spray coating, on the substrate was hydrolyzed at 75~$80^{circ}C$ in moisture cabinet (80~90 % humidity) to form the multicomponent gel. The films up to about 0.8~1.0$mu extrm{m}$ in thickness can be obtained by repeating operation, spraylongrightarrowhydrolysis and condensationlongrightarrowdryinglongrightarrowheating and crystallization at $700^{circ}C$ for 3~5min. The far-infrared radiation spectra of the coated films on substrate were examined by FT-IR and of films was also observed by scanning electron micrograph technique. The thermal evaluation of the gel-film is followed by TG/DTA measurements. The structure evaluation is followedd X-ray diffraction. These results suggest that this process is applicable to far-infrared radiat at thin film technique.