To develop VLSI of higher packing density with 0.5.mu.m gate length of less, semiconductor devices require shallow junction with higher doping concentration. the most common method to form the shallow junction is ion implantation, but in order to remove the implantation induced defect and activate the implanted impurities electrically, ion-implanted Si should be annealed at high temperature. In this annealing, impurities are diffused out and redistributed, creating deep PN junction. These make it more difficult to form the shallow junction. Accordingly, to miimize impurity redistribution, the thermal-budget should be kept minimum, that is. RTA needs to be used. This paper reports results of the diffusion characteristics of PSG film by varying Phosphorus weitht %/ Times and temperatures of RTA. From the SIMS.ASR.4-point probe analysis, it was found that low sheet resistance below 100 .OMEGA./ㅁand shallow junction depths below 0.2.mu.m can be obtained and the surface concentrations are measured by SIMS analysis was shown to range from 2.5*10$^{17}$ aroms/cm$^{3}$~3*10$^{20}$ aroms/cm$^{3}$. By depending on the RTA process of PSG film on Si, LDD-structured nMOSFET was fabricated. The junction depths andthe concentration of n-region were about 0.06.mu.m. 2.5*10$^{17}$ atom/cm$^{-3}$ , 4*10$^{17}$ atoms/cm$^{-3}$ and 8*10$^{17}$ atoms/cm$^{3}$, respectively. As for the electrical characteristics of nMOS with phosphorus junction for n- region formed by RTA, it was found that the characteristics of device were improved. It was shown that the results were mainly due to the reduction of electric field which decreases hot carriers.