In order to compare mechanical properties of ausformed martensite with those of marformed martemsite in Fe-30%Ni-0.1%C alloy and to investigate their strengthening mechanisms, ausformed martensite and marformed martensite were prepared by ausforming treatment and marforming treatment respectively. The microstructures were observed and the quantities of retained austenite, hardness, yield strength, ultimate tensile strength and elongation were examined. The strength of ausformed martensite was mainly increased because of the lattice defects inherited from austenite. The ductility of ausformed martensite was constant at the rate of 7-8% by ductile matrix formation of the retained austenite in spite of the increase in strength. The strength of marformed martensite was increased by the increment in dislocation density, the crossing of transformation twin with deformation twin and the mutual crossing of deformation twin. The ductility of mar formed martensite was slightly lower than that of ausformed martensite, but the strength of mar formed martensite was prominently higher.