Most investigators recommended that porcelain surface should be roughened with abrasives and/or be etched with acid in repairing the fractured porcelain with composite resin. This study was designed to evaluate the effect of porcelain surface treatments on the bond strength between porcelain and composite resin by measuring the shear bond strength and observing the porcelain surface with SEM. 48 porcelain disc were fabricated with Vintage porcelain and embedded in epoxy resin with the test surface exposed. The specimens were divided four groups at random and the test surfaces of the four groups were prepared as follows : Group 1 : Porcelain surface was roughened with a fine diamond and treated with 32% phosphoric acid gel for 10 seconds. Group 2 : Porcelain surface was roughened with a fine diamond and etched with 8% hydrofluoric acid gel for 5 minutes. Group 3 : Porcelain surface was roughened with a coarse diamond and treated with 32% phosphoric acid gel for 10 seconds. Group 4 : Porcelain surface was roughened with a coarse diamond and etched with 8% hydrofluoric acid gel for 5 minutes. All specimens were washed for 30 seconds. A representative specimen of each group was selected and the porcelain surface was observed with SEM at 1000 magnification. Remaining specimens were silanated, bonded with composite resin, thermocycled, and shear-tested on specially designed zig connected to Instron machine. The results were as follows : 1. The shear bond strength of the group etched with hydrofluoric acid was significantly higher than that of group treated with phosphoric acid(p<0.01). 2. The shear bond strength of the group roughened with a fine diamond was not significantly different from that of the group roughened with a coarse diamond(p>0.01). 3. SEM examination of prepared porcelain surfaces revealed that the surface etched with hydrofluoric acid showed numerous microporosities, undercut, and rougher surface than the surface treated with phosphoric acid. 4. All specimens etched with hydrofluoric acid showed cohesive failure within porcelain, but specimens treated with phosphoric acid mainly showed adhesive failure between porcelain and composite resin.