The purpose of this study was to evaluate and compare film thickness of five kinds of resin luting cements [Comspan, Panavia Ex, Maryland bridge adhesive, All-bond C & B cementation kit, and Super-bond C & B]. Zinc-phosphate cement and glass-ionomer cement were used as the control group. In order to measure the film thickness the methods used were in broad compliance with ADA Specification No. 8, a tapered-die system that simulates clinical conditions more closely, and the connected tapered-die system that simulates bridge conditions. The inorganic filler size of resin cements was also examined with scanning electron micrographs. The results were obtained as follows ; 1. The film thickness of resin cements was increased in the order of Comspan, Panavia Ex, Super-bond C & B, Maryland bridge adhesive, and All-bond C & B cementation kit. Maryland bridge adhesive and All-bond C & B cementation kit showed significantly higher film thickness than the control group(p<0.01). 2. For all resin cements, there was a significant difference of film thickness between the ADA method and the tapered-die system. Generally, the tapered-die system demonstrated lower film thickness than the ADA method(p<0.01). 3. There was no significant difference in film thickness between the tapered-die system and the tapered-die bridge system in all resin cements(p<0.01). 4. The scanning electron microscope showed that the cement with larger filler had a tendency to be higher in film thickness.