To accelerate the cure of phenolic resin adhesives for plywood, the complexation with melamine resin and the addition of cure-accelerating agents were discussed. The hot-pressing temperature and time of phenol resin could be decreased by complexation with melamine resin. but the wet glue-joints strength of phenol melamine resin was lower than that of ordinary phenol resin in case of plywood using spruce veneer at core layer. Among the tested cure-accelerating agents. the sodium carbonate showed the greatest effect on shortening gelation time of phenolic resin. In addition, in the manufacturing scale test, the hot-pressing time of phenol resin with the addition of 5 parts sodium carbonate could be shortened about 20% compared with ordinary phenol resin which had same glue-joints properties.