This paper was performed to study the utility of the SP(small punch) test and the AE(acoustic emission) test in the evaluation of SCC(stress corrosion cracking) susceptibility for parent metal and bond line of HT80 steel-weld joint by SAW(submerged arc welding) with the various pH values. The loading rate used was 3*10$^{-4}$ mm/min and the corrosive environment used was synthetic sea water during the SP test and the AE test. According to the test results, the SCC susceptibility of the parent metal was increased in the order of pH6.0, pH8.2 and pH10.0. On the other hand, the bond line showed almost the same high SCC susceptibility in all pH concentrations. Synthetically, from the results of the SCC susceptibility, the macro- and micro-SEM observation, the microfracture behaviors by AE test and the relationship between SCC susceptibility and displacement at incipient failure, .delta.$_{i.f-AE}$, it can be concluded that the SP test and the AE test are the good test methods to evaluate the SCC susceptibility for parent metal and bond line of the weld joint with the change of environmental factors.