The dynamic stress intensity factors (DSIF ; $K_{I}$$^{dyn}$) were studied in some polymeric materials using caustics method with a high speed camera system. Also crack tip propagation speed was measured by dynamic crack propagation velocity measuring device. To calculate DSIF a finite element analysis program-INha Stress Analysis Moving CRack(INSAMCR) was utilized. Dynamic fracture characteristics were investigated to verify a relationship between DSIF and crack tip propagation speed and acceleration in PMMA, Homalite-100 and Polycarbonate. The relationship between dynamic stress intensity factor and crack tip velocity revealed typical shapes. Measured crack tip acceleration data envelope converges to the zero level with increasing DSIF. Equivalently crack tip velocities show a wide spread range at low values of DSIF, but become a constant with a higher DSIF. 1.2MPa.root.m, 1.4MPa.root.m and 1.3 MPa.root.m were obtained as $K_{I}$$^{dyn}$ values to arrest the dynamic crack for PMMA, Homalite-100 and Polycarbonate, respectively. INSAMCR was run to verify experimental results in PMMA and shows good agreementmentment