Transparent xBa(La$_{1}$2/Nb$_{1}$2/)O$_{3}$-(1-x)Pb(Zr, Ti)O$_{3}$ (x=8.5, 9.0[mol.%], Zr/Ti=70/30~40/60) ceramics were fabricated by the two-stage sintering method, the electrooptic properties were investigated with Ba(La$_{1}$2/Nb$_{1}$2/)O$_{3}$ content and Zr/Ti composition ratio. Decreasing the Zr/Ti ratio, the electrooptic property was changed from a quadratic electrooptic effect to a linear electrooptic effcet. In the BLN-PZT 9.0/50/50 specimen having the tetragonal structure, the linear electrooptic coefficient had the highest value of 6.01*10$^{-10}$ [m/V] and in the BLN-PZT 9.0/55/45 specimen which located near the MPB region, the quadratic electrooptic coefficient had the highest value of 10.53*10$^{-16}$ [m$^{2}$/V$^{2}$].