Strontium titanate single crystal was grown by floating wne method. Growth conditions are as follows; at air atmosphere, rotation rate of upper and lower shafts were 20 - 25 rpm, 15 - 20 rpm respectively and growth rate was 3 mmlhr. As grown crystal was light brown color and transparent. After annealing, color was faded away. Growth direction was [112] direction and it was confirmed that grown crystal has $SrTiO_3$single phase and stoichiometric composition by XRD and EDS. Etch pit pattern was investigated after chemical etching in $350^{circ}C$, KOH solution for 5 min and dielectric constant was measured at the range of room temperature ~ $350^{circ}C$ .