The microstructure and electrical propetries were investigated for polycrystalline $Ba^{1-x}Sr_xTiO_3$(BST) thin films deposited on Pt/Ti/$SiO_2$(PTSS) and Pt/MgO(PM) substrates by metalorganic chemical vapor deposition (MOCVD). BST films on PTSS have coulmnar and porous structures, while on PM have an equiaxied and dense structure. The dielectric constant and a dissipation factor of BST films on PTSS and 20 fC/$mu extrm{cm}^3$ on PTSS and 12fC/$mu extrm{cm}^2$ on PM was obtained at an applied electric field of 0.06 MV/cm. Leakage current density of BST films on PM was smaller than that on PTSS. The leakage current density level was about $8 imes10^{-8}A/ extrm{cm}^2$ at 0.04MV/cm.