The effect of WO3 addition on microwave dielectric properties of BaTiO3-3{(1-x)TiO2-xWO3} system was studied. Addition of WO3 to this system resulted in the formation of BaWO4 and Ba2Ti9O20 phases. Both the dielectric constant (K) and the temperature coefficientof resonant frequency (Tf) were decreased with the amount of WO3 addition. The value of Q$ imes$f0 was increased as the amount of WO3 was increased up to x=0.0275, and then decreased when x exceeded 0.03. At x=0.0275, this ceramic showed excellent microwave proprties of K=34-35, Q$ imes$f0=50,000-53,000, and near zero ppm/$^{circ}C$ of Tf.