In this research, the emphasis was focused on the rearrangement and densification behavior of CaO particles when the aluminum was added to improve the hydration resistance. For the case of 0.5vol% Al added specimen, the rearrangement of CaO particles due to liquid aluminum was terminated near 140$0^{circ}C$ where the theoretically calculated fractional volume of solid reached 0.74 under Ar atmosphere. The density of the specimen sintered at 155$0^{circ}C$ for 5hrs reached 96% of relative theoretical density when the ambient was switched to O2 at intermediate and final stages of the sintering. The weight gain due to the hydration after 60 days under 72% of relative humidity at 26$^{circ}C$ was less than 1%.