The new forming method, Pressureless Powder Packing Forming Method was applied to the manufacturing of reaction sintered SiC. After the experiments of vibratory powder packing and binder infiltration, the abrasive SiC powder of which mean size is 45${mu}{ extrm}{m}$ was selected to this forming method. Uniform green bodies with porosity of 45% and narrow pore size distribution could be formed by this new forming method. Also, complex or varied cross-sectional shapes could be easily manufactured through the silicone rubber mould used in this forming method. Maximum 15 wt% amorphous carbon was penetrated into green body by multi impregnation-carbonization cycles. And reaction-bonded SiC was manufactured by infiltration of SiC-carbon shaped bodies with liquid silicon.