TiB2 was simultaneously synthesized and densified with concurrent self-propagating high-temperature synthesis and direct contact-heating by electrcial power input and pressure. Density of TiB2 synthesized by self-propagating high-temperature synthesis and consolidated simultaneously by direct contact-heating and pressure was maximum 80% of the theoretical density (4.52g/㎤). Temperature profile was analyzed by solving heat balance equation with numerical method (FTCS method). The temperature of the sample was sufficiently raised to that temperature sufficient to be densified. It was ascertained that the density of the SHS synthesized TiB2 is exponentially proportinal to the input thermal energy per mass.