Cavitation erosion-corrosion implies damage to materials due to the shock pressure or shock wave that results when bubbles form and collapse at a metal surface within a liquid. If the liquid is corrosive to the material, a condition typically encountered in industry, the component materials may suffer serious damage by a combination of mechanical and electrochemical attack. In this study, the mild steel(SS41) was tested by using the piezoelectric vibrator with 20kHz, 24$mu$m to cavity generation apparatus. The damage behaviour of vibration cavitation erosion-corrosion and the environment characteristics were investigated in various solutions which are seawater, tap water and distilled water. The main results obtained are as follows; 1) The cavitation erosion-corrosion damage behaviour in the seawater increases to occur at the equal degree on the middle portion and the outside portion of specimen. The distilled water specimen, on other hand, occurs beginning on the outside portion across to the middle portion of specimen. 2) The cavitation erosion-corrosion damage in the tap water of low specific resistance more increases than that in the distilled water of high specific resistance at the initial testing time and more decreases than that in it by the CaCO sub(3) film with testing time. 3) Cavitation erosion-corrosion damage characteristic divides into four regions; incubation region, acceleration region, deceleration region and steady state region.