Using the acetate velvet and viscose velvet whose pile lengths were sheared as 1.45, 1.55, 1 65, 1.75, 1.85, 1.90mm under the condition equating the weaving process of ground fabric, the conclusions were as follows through the results of the sensory assessments estimated by women students in our university and the physical properties, H. V and T. H. V obtained by KES-F system. 1. In the sensory assessments estimated by the method of paired comparison and ranking of samples, the longer pile length was, the more the hand values of smoothness, softness, thickness, heaviness increased on the whole. 2. The H V. and T. H. V. measured by KES-F system were as follows; Kohi increased to pile length 1.85mm and then decreased a little at 1.90mm. hummer increased as pile length was longer. Fukurami increased to pile length 1.75mm and then decreased gradually as pile length was longer. Total hand value increased gradually from 1. 45mm to 1.85mm, had the top value at 1.85mm, and then decreased a little at 1.90mm. 3. In the results of summarizing $ulcorner$the physical properties correlated closely with the H. V obtained by sensory assessments$lrcorner$ and tithe Physical properties correlated closely with the H. V. and T. H. V obtained by KES-F systems, it showed that all the sensory properties correlated closely with compressive energy, flexural rigidity, thickness, weight and pile ratio in the former and that the physical properties correlated closely with each H V and T. H. V were different in the latter. 4. It showed that factor 1 was related to compressive energy, thickness, weight, pile ratio, factor 2 was related to recovery energy, compressive resilience, compressive index, and factor 3 was related to compressive recovery ratio in the result of factor analysis. 5. In the multiple repression analysis, the expressions of all sensory properties had compressive ratio, frictional coefficient in the regression expressions of $ulcorner$H. V. obtained by sensory assessments$lrcorner$, while the expressions of each H. V. and different physical properties in the regression expressions of $ulcorner$H. V. obtained by KES-F system$lrcorner$.