The magnetic properties of Mg-Mn ferrites were investigated in the composition range of $Mg_{a}Mn_{b}Fe_{c}O_{4pmdelta}$ (a+b+c=3) with the addition of $Al_{2}O_{3}$. In $MgO-MnO-Fe_{2}O_{3}$ ternary system, the spinel single phase existed within the composition range of MgO-50 mol%, MnO-70 mol% and $Fe_{2}O_{3}-60;mol%$. The saturation magnetic flux density increased with the increase of $Fe_{2}O_{3}$ content and showed the maximum at the stoichiometric composition of $(Mg,Mn)Fe_{2}O_{4}$. In $Mg_{x}Mn_{1-x}Fe_{2}O_{4}(x=0.2~0.8)$ system, the saturation magnetic flux density showed the maximum at $Mg_{0.2}Mn_{0.8}Fe_{2}O_{4}$. The addition of $Al_{2}O_{3}$ resulted in the decrease of saturation magnetic flux density but increased the electrical resistivity.