PTCR(Positive Temperature Coefficient of Resistivity) thermistor in thin film BaTiO$_{3}$ system was prepared by using radio frequency(13.56 MHz) and DC magnetron sputter equipment. Polycrystalline, surface structure, and R-T(Resistivity-Temperature) characteristics of the specimens were measured by X-ray diffraction(D-Max3, Rigaku, Japan), SEM(Scanning Electron Microscopy: M.JSM84 01, Japan), and insulation resistance measuring system (Keithley 719), respectively. Thin films characteristics of the thermistor showed different properties depending on the substrate even with the same sputtering condition. The thin film formed on the A1$_{2}$O$_{3}$ substrate showed a good crystalline and a low resistivity at below curie point. However, the thin films prepared on slide glass and Si wafer were amorphous. The thicknesses of the three samples prepared under the same process conditions were 700[.angs.], 637.75[.angs.], and 715[.angs.], respectively.