The optical and electrical properties of $C_{22}$-Quinolinium(TCNQ) Langmuir-Blodgett films have been studied depending on the annealing temperatures. The optimal properties were investigated using UV/visible(300-800[nm]) absorption spectra and FTIR(Fourier-transformed- infrared) absorption measurements. The electrical properties were investigated in a frequency range of 10[Hz]-13[MHz]. The UV/visible absorption spectra at room temperature show that there are four characteristic peaks at 320, 380, 494 and 678[nm]. These absorption peaks decrease very rapidly above the annealing temperature of 180[.deg. C], which is due to a structural change of TCNQ. The FTIR absorption measurements strongly support the result of the UV/visible absorption spectra, because the absorption peak of TCNQ- at 2181[$cm^{-1}$ /] also decreases above 140[.deg. C]. The frequency-dependent dielectric constant shows that there is a dielectric dispersion near 1[MHz] which is due to an orientational polarization of the molecules inside the film. The overall frequency-dependent dielectric constant is higher near 80[.deg. C]. It may be due to a softness of the alkyl chains.s.