This paper describes a study on absorption properties of electromagnetic wave by the composition ratio of Ni-Zn ferrite. Ni-Zn ferrite was composed of 48-52mol% Fe$\_$2/O$\_$3/, 18-22mol% NiO and 26-34mol% ZnO. The sintering of the composition was carried out at 1200.deg. C for 2 hours. Through the experiments, it was found that the resonance phenomenon occured at low frequency range for high permeability and vice versa. In the case of the composition of 49mol% Fe$\_$2/O$\_$3/, 20mol% NiO and 31mol% ZnO, the bandwidth ranged from 0.35GHz to 0.95GHz with the absorption thickness of 10mm. Also, in the case of the composition 51mol% Fe$\_$2/O$\_$3/, 22mol% NiO and 27mol% ZnO, the bandwidth ranged from 0.48GHz to 1.2GHz with the absorption thickness of 6mm.