The hygrothermal effect on three different types of Glass/Polypropylene was investigated under the environment of 4$0^{circ}C$ distilled water. The residual strength of Glass/Polypropylene with randomly oriented and fiber content of 4-wt%(R40) was found stable under the moisture content of 0.2%. In this case, the maximum moisture content was 0.53%. On the other hand, Glass/Polypropylene with unidirection and 42wt%(U42) and 50st%(U50) fiber content, respectively, showed the residual strength less stable than R40. However, the maximam moisture contents were 0.52% and 0.45% respectively.