Using the Si/SiGe layer grown by solid source molecular beam epitaxy(SSMBE) on the LOCOS-patterned wafers, an emitter-base self-aligned hterojunction biplar transistor(HBT) with the polysilicon-emitter and the silicon germanium(SiGe) base has been fabricated. Trech isolation process, planarization process using a chemical-mechanical poliching, and the selectively implanted collector(SIC) process were performed. A titanium disilicide (TiSi$_{2}$), as a base electrode, was used to reduce an extrinsic base resistance. To prevent the strain relaxation of the SiGe epitaxial layer, low temperature (820${^circ}C$) annealing process was applied for the emitter-base junction formation and the dopant activation in the arsenic-implanted polysilicon. For the self-aligned Si/SiGe HBT of 0.9${ imes}3.8{mu}m^{2}$ emitter size, a cut-off requency (f$_{T}$) of 17GHz, a maximum oscillation frequency (f$_{max}$) of 10GHz, a current gian (h$_{FE}$) of 140, and an emitter-collector breakdown voltage (BV$_{CEO}$) of 3.2V have been typically achieved.