In this paper the manufacture of shrinkage-free in situ Mullite-ZrO$_2$ceramics through the addition of Al base metal powder to the mixture of ZrSiO$_4$and A1$_2$O$_3$was attempt. The ZrO$_2$-strengthened mullite ceramics was prepared after the following reaction form, 3(Al+Al$_2$O$_3$)+2ZrSiO$_4$longrightarrow3A1$_2$O$_3$.2SiO$_2$+2ZrO$_2$Al metal powder was added from none to 30 weight percent to the A1$_2$O$_3$. The powders were mechanically mixed, isostatically pressed and reaction sintered at 1450-1$600^{circ}C$ for 3hours. The specimens were sintered with and without intrim soaking time for 5 hours at 125$0^{circ}C$ for the oxidation of Al-powder The addition of aluminium accelerates the reaction and compensate the shrinkage during the sintering through an increase in volume of oxidized Al. Because coarse flake type Al metal powders were not effectively milled, oxidized Al resulted in the relative large pore in the specimen.