To increase the capacity of positive electrode materials for matching the high capacity negative electrode materials in alkaline rechargeable batteries, high-density nickel hydroxide powders were made through a continuous process from nickel sulfate reacted with ammonia and sodium hydroxidc. The effect of operating conditions on structure, shape, size distribution, apparent density and tap density of powders were investigated. Crystal structure of nickel hydroxide powder was hcp according to Bravais Lattice. The increase of mean residence time promoted the growth of (101) plane. The shape of powder was nearly spherical. Their size was in the range of $2~50mu extrm{m}$. The size distribution of the powders prepared was narrower than that of commercially obtained nickel hydroxide. Apparent density and tap density were 1.6~1.7g/cc and 2.0~2.1g/cc, respectively.