To investigate the effects of pretreatment and substrate bias on the characteristics of the diamond thin films, the thin films were deposited on the p-type Si(100) wafer by MPECVD using mixtures of $H_2$, $CH_4$, and $O_2$ gases. Deposition was carried out at the substrate temperature of $900^{circ}C$ and at the pressure of 40torr. The effect of the pretreatment on the film formation was the examined by using SiC and diamond powders as abrasive powders. Furthermore, the substrate bias effect on the formation of the diamond film was also examined. The highest nucleation density was observed for the pretreatment with 40~60$mu extrm{m}$ size of diamond powders and a negative bias potential(-50V). Many defects and(111) twins in the diamond films were observed.