A nickel mesh and an expanded nickel sheet were used as a current collector for supporting active materials of cathode in rechargeable batteries, while a porous nickel substrate was extensively studied because of its 3-dimensional structure which has high capabilities for active materials and current collection. Optimum coating conditions were studied by SEM and two step d. c. constant current electrolysis for the graphite coating and electro-plated nickel on an urethane substance which was highly porous and 3-dimensional structure. The density and the porosity of nickel support obtained by using two step current density and 80 ppi urethane substance were 0.38∼0.40 g /㎤ and 94∼96%, respectively. It was possible to fabricate a highly porous and good packable nickel substrate using two step current density and surfactants at sulfamic acid nickel plating bath.