We were studied to the effect of alloying element and retained austenite on a mechnical properties and that used steels were composed three types composition. According to the soaking temperature, a retained austenite was pricipitated in the bainitic ferrite matrix and it was pricipitated to a flake type of about $2{mu}m$, a mixture of massive and bar type and a flake type of about $1{mu}m$ size. Through x-ray diffraction analysis, the amount of retained austenite was increased with addition of Si and Ni for equal heat treatment condition and it was best abundanted in the soaking temperature of $855^{circ}C$. The balance value of strength and elongation were complexly controlled not only a retained austenite formation but also a formation characteristic and shape of the retained austenite and bainite. The balance value of strength and elongation were most satisfactory obtained with "B" and "C" specimens in a firstly heat treated at $855^{circ}C$ and the best result was that a $2840kg/mm^2.%$ with the heat teratment condition of $855^{circ}C-400^{circ}C$ used for "C" specimen.