The reduction and diffusion process(R-D process) is an economical way to produce the functional materials which contain rare-earth elements and has been applied to the production of rare-earth magnet meterials($SmCo_5$, $Nd_{15}Fe_{77}B_8$), magneto-optical(MO) target materials and hydrogen storage alloy, etc. However, because of difficult to control of the final composition, the R-D process has not been applied to production of the 2-17 type rare earth permanent magnet materials which contain several elements. Therefore, this work was as a basic study for the production of the 2-17 type rare earth permanent materials with composition $Sm(Co_{0.72}Fe_{0.21}Cu_{0.05}Zr_{0.03})_{7.9}$ by the R-D process, the following were mainy examined ; the amount of metallic calcium as a reductant, homogenization condition of the alloy after the R-D reaction, masuring of magnetic properties of the sample after step aging. The sample prepared by the R-D process contained a little more oxygen than that prepared by the melting method, however, showed almost the same magnetic properties.