The influence of deposition parameters on the deposition of $SnO_2$ thin films by spray pyrolysis has been studied. In the case of spray solution with tile concentration of 0.01M, at low deposition temperature the deposition was controlled by surface reaction and portion controlled by mass transfer is increased with increasing deposition temperature to $400^{circ}C$. Above $400^{circ}C$, the deposition is controlled by mass transfer at low spray pressure, and by surface reaction at high spray pressure. As the concentration of spray solution increased the deposition rate increased, and in this experiment the deposition depends on the Rideal-Eley mechanism. The deposition rate increased with increasing substrate temperature up to $400^{circ}C$ and then decreased due to homogeneous nucleation. The thickness of the deposit increased with increasing spray duration, and the adhesion between substrate and deposit was formed physically.