Since heat curing acrylic resins undergo unavoidable dimensional changes following polymerization, adaptation can be altered. Until recently, although numerous studies on the dimensional changes of denture base were based on a microscopic technic that measures the relative displacement of a limited reference points on the denture base, but there have been few studies on the distortions of resins using holographic interferometry. Purpose of this study was to determine and compare the dimensional changes and fringe patterns of 4 heat curing acrylic resins, and observe the distortions of acrylic resin denture base by temperature change with the aid of the holographic interferometry. Holographic interferograms were taken on the resin specimens and acrylic resin denture base with the 10mW He-Ne laser and double exposure method. Comparison and analysis of fringe pattern on the recorded object surface was performed. The following results were obtained. 1. The dimensional changes for the high impact resin Lucitone 199 were statistically the greatest of all resins, and the rapid heat curing resin Premium super 20 were the least. 2. The most polymerization shrinkage of all materials occured in initial period of measurements, at this time the difference of polymerization shrinkage properties between resins was founded. 3. The stress distribution of specimens was seen by various type of fringe pattern which had directionality. 4. The polymerization shrinkage of resins was greatly influenced by temperature change. 5. The partial deformations of resin denture base were observed in 70 C and 90 C water.