The purpose of this study was to investigate the effect of stannous fluoride on the dentin bonding with three kinds of commercially available dentin bonding systems containing different adhesive monomers. Dentin specimens with exposed labial dentin prepared from freshly extracted bovine mandibular anterior teeth were divided into experimental and control groups. The specimens of experimental groups were bonded with dentin bonding systems and composite resins including All bond 2 ㅡ& Bisfil, Scotchbond Multi-Purpose & Z100, and Denthesive II Charisma after 2 % stannous& fluorided application for S minutes and washing for 1 minute. The specimens of control groups were bonded with the same dentin bonding systems and composite resins as used in the experimental groups. After bonded specimens were stored in $37^{circ}C$ distilled water for 24 hours, the tensile bond strength and cohesive failure rate were measured, and then the pretreated dentin surfaces and the fractured dentin surfaces were examined under scanning electron microscope. The results were as follows : Mean bond strength of stannous fluoride applied groups of All bond 2, Scotchbond MP, and Denthesive II were 2.5MPa, 1.1MPa, and 1.1MPa respectively, and those of control groups were 7.5MPa, 8.1MPa, and 4.6MPa. Bond strength values of stannous fluoride applied groups were significantly lower than those of the control groups(p<0.05). SEM findings of dentin surfaces after stannous fluoride application demonstrated an appearance of partially remained smear layer and smear plugs inspite of pretreatment with 10 % phosphoric aicd or maleic acid solution, and an appearance of smear layer covered surface under Denthesive II priming. But those of control groups commonly showed clean dentin surfaces without smear layer and smear plugs. On SEM observation of the fractured dentin-resin interface, while most of the specimens of stannous fluoride applied groups showed adhesive failure mode, those of All bond 2 and Scotchbond MP control groups showed mainly adhesive-cohesive mixed failure mode, and mainly adhesive failure mode in Denthesive II control group.