The purpose of this study was to evaluate the adaptation of light cured dentin bonding agents to tooth structure by measuring contraction gaps on interfaces between cavity wall and composite resin under SEM study. In this study, class V cavities with cementum margin were prepared on the buccal surfaces of 15 extracted human premolar teeth and teeth were randomly assigned 3 groups of 5 teeth each. The cavities were filled with three dentin bonding agents and two composite resins were investigated for this study: three dentin bonding agents; Scotchbond 2, Scotchbond Multi-Purpose. All-Bond 2, two composite resins; Silux Pius, Z-100. Group 1 : Scotchbond 2 + Silux Plus Group 2 : Scotchbond Multi~Purpose + Z-100 Group 3 : All-Bond 2 + Z-100 The restored teeth were stored in 100% relative humidity at $37^{circ}C$ for 7 days. And then, the roots of the teeth were removed with the tapered fissure bur and the remaining crowns were sectioned occlusogingivally through the center of restorations. Adaptation at tooth-restoration interface was assesed occlusally, gingivally, and axially by scanning electron microscope. The results were as follows : 1. In Group 1, the adaptation to dentinal wall of Scotchbond 2 was poor, but the adaptation to enamel wall of Scotchbond 2 was excellent. 2. In Group 2, the adaptation to occlusal was axial wall and gingival wall of Scotchbond Multi-Purpose was excellent. Especially in axially wall, the dentin bonding agents infiltrated into dentinal tubules and there was excellent adaptation to dentinal wall. 3. In Group 3, the adaptation to occlusal wall and axial wall of All-Bond 2 was excellent. But in gingival wall, there was gap formation between composite resin and dentin bonding agent.