This study was designed to etermine the changes in the degree of conversion for composite resins after heat curing following the methods proposed by Lee & Park(1995). 8-mm diameter hole was made in 1mm teflon plate and one of three types of composites (Charisma, Brilllant, Z100) was placed and light cured for 60seconds. The samples were devided into 3 groups according to the placing composites. After light curing, the samples were separated from the moulds. Using this method, 10 samples were prepared in each group; 5 samples from each group were heat cured according to the methods proposed by manutfactures, These samples were then thinned to 50-$70{mu}m$ and analysed with a Fourier Transform Infrared Spectrometer. Standard baseline technique was used to calculate the degree of conversion. When the samples were light cured, the degrees of conversion in each groups were 47.1 % (charisma), 53.3% (Z100), and 70.1 % (Brilliant). The degree of conversion after heat curing were; 60.1 % (Charisma), 71.1 % (Z100), and 73.3 % (Brillant). Once the samples were heat cured, there were significant increases in degree of conversion.