The purpose of this study was to asses the shear bond strengths of 3 types of light-curing Glass Ionomer cement to dental amalgam with or without an intermediary agent. 60 amalgam adherent specimens were prepared and aged in water at $37^{circ}C$ for 3 days. Before bonding, the amalgam surfaces were finished flat on 600-grit silicon carbide paper. 30 specimens among 60 were used for bonding in this condition, and the other 30 were covered with a thin layer of light-curing intermediary agent. Shear bond strengths were measured with universal testing machine (Instron, Model 4301) and statistically processed by ANOVA and t-test. On completion of bond test, the fracture surfaces were examined under light microscope so that the mode of bond failure could be assessed The results were as follows : 1. Bond strength of Fuji II LC group showed the hightest value and was followed by Vitremer, Vitrebond groups (p<0.05). 2. The bond strengths achieved without an intermediary agent were higher than those obtained with intermediary agent (p<0.05). 3. For the specimens bonded with intermediary agent, bond failures occured mostly at the agent-amalgam interface. So, the use of intermediary bonding agent was thought not recommendable at glass ionomer-amalgam interface.