The spot weldability of coated steels for automobile has been investigated. Coated steels of SPC-Zn DC, SPC Zn-Ni SC, SPC Zn-Ni DC, SPC Zn-Fe DC and OCCS were welded under different conditions of welding current, force and time. Coating thickness at the welded surface was reduced as increased welding current. Tensile shear strength(TSS) and cross tensile strength (CTS) were increased up to expulsion began, then dropped as increased current. Optimum conditions of welding force and time were different, however 200~250kgf and 15~20cycle were optimum for coated SPC (Steel Plate Cold). Weldability lobes were measured for each coated steel and they showed narrow range of working welding current. The organic composite coated steel (OCCS) had the highest current to get $sqrt5{t}$ nugget size and narrowest working welding current range.