For the case of creep-fatigue interaction, the damage zone developed in front of the growing crack-tip during creep regime is important because it can affect the damage mechanism to be occured by the following fatigue load. These are studied in theis paper through proper consideration of the cavitiy-size dependent sintering stress which is approximated by polynomials. It is shown that the inclination of reversed damage zone size with respect to the applied load parameter can be explained by considering realistic sintering stress distribution. However, the resultant stress field has $r^{1/2+ heta}$ singularity, regardliss of the profile of variable sintering stress, which is the same to that case solved for constant sintering stress.